Product Details:
Minimum Order Quantity | 1000 Kilogram |
Application | Manufacturing, Forged flanges, Fittings, Construction, School/College Workshop |
Material Grade | ASTM A350 LF2 |
Thickness/Diameter | >4 inch, 1-2 inch, 2-3 inch, 3-4 inch, 0-1 inch |
Single Piece Length | 6 meter, 3 meter |
Brand | Jayant, Imported |
Chemical Composition(Chemistry) of ASTM A350 LF2 | C 0.30Max, Mn 0.60-1.35, Si 0.15-0.30, P 0.035Max, S 0.040Max, Cr 0.30Max, Ni 0.40Max, Mo 0.12Max |
Payment Terms | 100% Advance Against Proforma Invoice. Sorry no credits |
Third Party Inspection (TPI) | Allowed. Charges to be borne by buyer. |
Test Certificate | NABL Government approved laboratory reports can be provided. |
Tradewell Ferromet Pvt Ltd, Khopoli, Mumbai, Maharashtra, India can offer ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars.
ASTM A350 LF2 are used as pipeline steels and also in the production of forged flanges, fittings, rings. They are suitable for use down to –50ºF (LF2).
Forging properties of ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars:
LF2 grades would ideally be forged at around 2250-2300ºF (1230-1260ºC) and not forged below 1650-1700ºF (900-925ºC.)
ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars can be avail as continuous cast (CC), rolled, forged in annealed, quenched tempered condition with black or bright (peeled or proof machined) finish.
Size Specifications: Can offer ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars as mentioned below:
LF2 Round Bars can be offered from 10mm upto 1000mm in diameter depending on raw material availability in stock.
LF2 Square, Flat Rectangular Bars can be offered in width thickness from 10mm upto 700mm length from upto 6 meters depending on size.
Chemical composition(Chemistry) of ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars:
Element: Percentage
C: 0.30 Max
Mn: 0.60–1.35
Si: 0.15–0.30
P: 0.035 Max
S: 0.040 Max
Cr: 0.30 Max
Ni: 0.40 Max
Mo: 0.12 Max
V: 0.08 Max
Cb: 0.02 Max
Cu: 0.04 Max
Pb: 0.02 Max
Mechanical Properties of ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars:
TS Min psi (Mpa): 70,000 (485)
YS Min psi (Mpa): 36,000 (250)
EL (2″ Min): 22%
RA Min: 30%
Hardness, Bhn: Max 197
-50ºF Charpy: Min Impact
Set of 3 Specimen*: 15 (20)
For One Specimen: 12 (16)
WELDING/HEAT TREATMENT Properties of ASTM A350 LF2:
Heat treatment of pipeline steels will no doubt be done on a continuous basis, and after welding. The structure of these steels will be initially determined by the rolling/forging process. The pipeline itself will be supplied from hot-rolled steels, the flanges etc. from forgings. The actual welding process will be primordial in ensuring the suitability and security of the pipeline and its subsequent performance. Preheat and postheat treatments are essential.
The three grades listed here are easily weldable by all tried and tested methods.
MACHINABILITY Properties of ASTM A350 LF2:
In the case of forged fittings and flanges, these grades may be machined as required, and ongoing experience will determine if machining is best done on an as-forged structure, a normalized structure or an annealed structure. In either case, in view of the critical nature of the end use, advice should be taken from a recognized heat treatment company.
We can supply smaller quantities of ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars from our associated manufacturing unit in India.
If any requirements for ASTM A350 LF2 Carbon Steel Bars / LF2 Round Bars / LF2 Bars kindlydo contact us.